h1

001014386 001__ 1014386
001014386 005__ 20251008095450.0
001014386 0247_ $$2HBZ$$aHT031227485
001014386 0247_ $$2Laufende Nummer$$a44636
001014386 0247_ $$2datacite_doi$$a10.18154/RWTH-2025-06056
001014386 037__ $$aRWTH-2025-06056
001014386 041__ $$aEnglish
001014386 082__ $$a620
001014386 1001_ $$0P:(DE-588)1372935347$$aWu, Chengguang$$b0$$urwth
001014386 245__ $$aRole of interstitial atoms in microstructures and mechanical properties of TiNbZr and TiNbZrHfTa complex concentrated alloys$$cvorgelegt von Chengguang Wu, M. Sc.$$honline
001014386 260__ $$aAachen$$bRWTH Aachen University$$c2025
001014386 300__ $$a1 Online-Ressource : Illustrationen
001014386 3367_ $$02$$2EndNote$$aThesis
001014386 3367_ $$0PUB:(DE-HGF)11$$2PUB:(DE-HGF)$$aDissertation / PhD Thesis$$bphd$$mphd
001014386 3367_ $$2BibTeX$$aPHDTHESIS
001014386 3367_ $$2DRIVER$$adoctoralThesis
001014386 3367_ $$2DataCite$$aOutput Types/Dissertation
001014386 3367_ $$2ORCID$$aDISSERTATION
001014386 500__ $$aVeröffentlicht auf dem Publikationsserver der RWTH Aachen University
001014386 502__ $$aDissertation, Rheinisch-Westfälische Technische Hochschule Aachen, 2025$$bDissertation$$cRheinisch-Westfälische Technische Hochschule Aachen$$d2025$$gFak05$$o2025-06-30
001014386 5203_ $$aUm der wachsenden globalen Nachfrage nach Transport und Energie gerecht zu werden, ist die Entwicklung effizienterer Turbinen und Kernreaktoren erforderlich, die bei höheren Temperaturen betrieben werden können und extremen Bedingungen (z. B. H₂-Exposition) standhalten. In den letzten zehn Jahren haben sich refraktäre komplex konzentrierte Legierungen (engl.: refractory complex concentrated alloys, kurz: RCCAs), bestehend aus drei oder mehr Übergangselementen der Gruppen IV, V und VI, als vielversprechende Materialien erwiesen. Sie bieten eine breite Zusammensetzungsvielfalt und verbesserte mechanische Eigenschaften bei erhöhten Temperaturen im Vergleich zu herkömmlichen refraktären Legierungen. Die Sprödigkeit von RCCAs bei Raumtemperatur schränkt jedoch ihre praktische Anwendbarkeit erheblich ein. Aktuelle Studien zeigen, dass interstitielle Elemente maßgeblich zum spröden Verhalten von RCCAs bei Umgebungsbedingungen beitragen. Darüber hinaus verdeutlichen die starken Affinitäten zwischen interstitiellen Atomen und refraktären Elementen deren Einfluss auf die Mikrostruktur und Phasenstabilität, was wiederum die makroskopischen mechanischen Eigenschaften verändert. Diese Arbeit zielt darauf ab, ein tiefgreifendes Verständnis der Wechselwirkungen zwischen interstitiellen Atomen (insbesondere H) und RCCAs zu erlangen, wobei der Fokus auf deren Auswirkungen auf die Mikrostruktur, Phasenstabilität und mechanischen Eigenschaften liegt, um die Entwicklung von RCCAs mit optimierten Eigenschaften unter extremen Bedingungen voranzutreiben. (1) Wasserstoffaufnahme in TiNbZr-RCCA: In-situ Synchrotron Hochenergie-Röntgenbeugung kombiniert mit Dichtefunktionaltheorie zeigt eine durch Wasserstoff induzierte Gitterexpansion (stabil bei 500 °C) und eine Umwandlung (kubisch-raumzentriert zu raumzentrierte tetragonale beim Abkühlen) in TiNbZr RCCA. Wasserstoff besetzt bevorzugt die Tetraederlücken. Bei geordneter Verteilung von H im Kristallgitter, wird dieses tetragonal. (2) Wasserstoffunterstützte Spinodale Entmischung: In der untersuchten TiNbZrHfTa RCCA Legierung beeinflusst die Anwesenheit von H die spinodale Entmischung. Dadurch verändert sich die Phasenzusammensetzung und die Werkstoffhärte wird gesteigert. Ein thermodynamisches Modell zeigt, wie Wasserstoff zur Destabilisierung von Einphasenstrukturen beiträgt und so neue Möglichkeiten der Mikrostrukturmodifikation eröffnet. (3) Einfluss von Bor auf die Korngrenzenchemie: Die Segregation von Bor an der Korngrenze verändert die lokale chemische Zusammensetzung in TiNbZrHfTa-RCCA, reduziert die Streckgrenze und ermöglicht gleiten an der Korngrenze. Der verbesserte Gleittransfer durch Bor-Dotierung verdeutlichen den großen Einfluss, den gezielte Ausscheidungen auf die mechanischen Eigenschaften haben. (4) Erhöhung der Duktilität durch Sauerstoff induzierte nanoskalige chemische Heterogenität: Die interstitielle Einlagerung von Sauerstoff in TiNbZr-RCCA führt zur Bildung einer nanoskaligen chemischen Heterogenität, die sich in Ti-Konzentrationsfluktuationen manifestiert. Die Ti-angereicherten Bereiche wirken als starke Versetzungsbarrieren, was zu einer erhöhten Verfestigungsrate und gesteigerten Dehnratenempfindlichkeit führt, diese Effekte werden begleitet von einer Verfeinerung der Deformationsbänder begleitet. Die mikrostrukturellen Merkmale tragen gemeinsam zur verbesserten Duktilität bei, während die Streckgrenze erhalten bleibt, und stellen somit eine vielversprechende Strategie zur Überwindung Festigkeits-Duktilitäts-Kompromisses in RCCAs dar. Diese Ergebnisse unterstreichen die entscheidende Rolle interstitieller Atome bei der Beeinflussung der Mikrostruktur und Phasenstabilität, welche letztlich die makroskopischen mechanischen Eigenschaften prägen, und bieten eine Grundlage für die Entwicklung von RCCAs mit maßgeschneiderten Eigenschaften für anspruchsvolle Anwendungen.$$lger
001014386 520__ $$aTo address the growing global demand for transportation and energy, the development of more efficient turbine engines and power generators capable of operating at higher temperatures and tolerating extreme conditions (e.g., H2 exposure) is essential. Over the past decade, refractory complex concentrated alloys (RCCAs), consisting of three or more transition elements from groups IV, V, and VI, have emerged as promising materials due to the vast compositional versatility and superior mechanical properties at elevated temperatures compared to the conventional refractory alloys. However, the brittleness of RCCAs at room temperature significantly limits their practical applications. Recent findings indicate that interstitial elements contribute to the brittle behavior of RCCAs at ambient conditions. Moreover, the strong affinities between interstitials and refractory elements underscore the influence of these small atoms on microstructure and phase stability, which, in turn, alter macroscopic mechanical performances. This thesis seeks to offer an in-depth understanding of the interplay between interstitial atoms (especially H) and RCCAs, focusing on their effects on microstructure, phase stability, and consequent mechanical properties, to advance the design of RCCAs with optimized performance under extreme conditions: (1) Hydrogen Accommodation in TiNbZr RCCA: In-situ synchrotron high-energy X-ray diffraction combined with density functional theory reveal hydrogen-induced lattice expansion (holding at 500 °C) and transformation (body-centered cubic to body-centered tetragonal cubic structure upon cooling) in a TiNbZr RCCA. Hydrogen prefers to accommodate at tetrahedral sites, while the ordered distribution of hydrogen solutes results in the occurrence of tetragonality. (2) Hydrogen-Assisted Spinodal Decomposition: In a TiNbZrHfTa RCCA, hydrogen modulates nanoscale spinodal decomposition, creating chemical fluctuations and enhancing hardness. A thermodynamic model demonstrates the role of hydrogen in destabilizing single-phase structures, enabling novel microstructure tailoring strategies. (3) Boron Effects on Grain Boundary Chemistry: Boron segregation alters grain boundary chemistry in a TiNbZrHfTa RCCA, reducing yield strength and enabling grain boundary shear localization. Enhanced slip transfers upon boron doping highlight the role of segregation engineering in optimizing mechanical performance. (4) Ductilization via Oxygen-Induced Nanoscale Chemical Heterogeneity: The incorporation of oxygen interstitials in a TiNbZr RCCA induces the formation of nanoscale chemical heterogeneity, characterized by Ti concentration fluctuations. The presence of Ti-enriched regions strongly pins dislocation, resulting in an increase in strain-hardening rate and strain rate sensitivity, accompanied by the refinement of deformation bands. These microstructural characteristics collectively contribute to improved ductility while preserving yield strength, offering a promising strategy for overcoming the strength-ductility trade-off in RCCAs. These findings highlight the critical role of interstitial atoms in influencing microstructure and phase stability, ultimately shaping macroscopic mechanical performance, and providing a foundation for designing RCCAs with tailored properties for demanding applications.$$leng
001014386 536__ $$0G:(CSC)202106780003$$aCSC 202106780003 - China scholarship council (202106780003)$$c202106780003$$x0
001014386 588__ $$aDataset connected to Lobid/HBZ
001014386 591__ $$aGermany
001014386 653_7 $$ainterstitial atoms
001014386 653_7 $$amechanical properties
001014386 653_7 $$amicrostrucure
001014386 653_7 $$arefractory complex concentrated alloys (RCCAs)
001014386 7001_ $$0P:(DE-82)000488$$aRaabe, Dierk$$b1$$eThesis advisor$$urwth
001014386 7001_ $$0P:(DE-82)IDM02564$$aMa, Yan$$b2$$eThesis advisor
001014386 8564_ $$uhttps://publications.rwth-aachen.de/record/1014386/files/1014386.pdf$$yOpenAccess
001014386 8564_ $$uhttps://publications.rwth-aachen.de/record/1014386/files/1014386_source.doc$$yRestricted
001014386 8564_ $$uhttps://publications.rwth-aachen.de/record/1014386/files/1014386_source.docx$$yRestricted
001014386 8564_ $$uhttps://publications.rwth-aachen.de/record/1014386/files/1014386_source.odt$$yRestricted
001014386 909CO $$ooai:publications.rwth-aachen.de:1014386$$popenaire$$popen_access$$pVDB$$pdriver$$pdnbdelivery
001014386 9101_ $$0I:(DE-588b)36225-6$$6P:(DE-588)1372935347$$aRWTH Aachen$$b0$$kRWTH
001014386 9101_ $$0I:(DE-588b)36225-6$$6P:(DE-82)000488$$aRWTH Aachen$$b1$$kRWTH
001014386 9141_ $$y2025
001014386 915__ $$0StatID:(DE-HGF)0510$$2StatID$$aOpenAccess
001014386 9201_ $$0I:(DE-82)523110_20140620$$k523110$$lLehrstuhl für Werkstoffphysik und Institut für Metallkunde und Materialphysik$$x0
001014386 9201_ $$0I:(DE-82)520000_20140620$$k520000$$lFachgruppe für Materialwissenschaft und Werkstofftechnik$$x1
001014386 961__ $$c2025-10-06T14:44:51.587283$$x2025-07-08T16:21:51.510105$$z2025-10-06T14:44:51.587283
001014386 9801_ $$aFullTexts
001014386 980__ $$aI:(DE-82)520000_20140620
001014386 980__ $$aI:(DE-82)523110_20140620
001014386 980__ $$aUNRESTRICTED
001014386 980__ $$aVDB
001014386 980__ $$aphd