245 _ _ |a Entwicklung prozessoptimierter Werkzeugtechnologien anhand eines seriennahen Zielbauteiles beim Thixoschmieden von Stahl
|c vorgelegt von Christophe Jean Daniel Beyer
|h online, print
260 _ _ |a Aachen
|b Publikationsserver der RWTH Aachen University
|c 2006
300 _ _ |a XI, 134 S, : Ill., graph. Darst.
336 7 _ |0 PUB:(DE-HGF)11
|2 PUB:(DE-HGF)
|a Dissertation / PhD Thesis
|b phd
|m phd
336 7 _ |0 2
|2 EndNote
|a Thesis
336 7 _ |2 DRIVER
|a doctoralThesis
336 7 _ |2 BibTeX
|a PHDTHESIS
336 7 _ |2 DataCite
|a Output Types/Dissertation
336 7 _ |2 ORCID
|a DISSERTATION
500 _ _ |a Zsfassung in dt. und engl. Sprache
502 _ _ |a Aachen, Techn. Hochsch., Diss., 2006
|g Fak05
|o 2006-02-15
520 3 _ |a Durch das Thixoschmieden können die Verfahrensvorteile von Schmieden und Gießen genutzt werden. So können beispielsweise komplexe Geometrie, die bislang in 4 bis 5 Arbeitsgängen hergestellt werden, in ein bis zwei Arbeitgängen dargestellt werden. Im Gegensatz zur Formgebung von Aluminiumlegierungen im teilerstarrten Zustand bestanden beim Thixoschmieden von Stählen bei den derzeit verfügbaren Formwerkzeugen noch beträchtliche Probleme bezüglich der mechanischen, tribologischen, chemischen und thermischen Leistungsfähigkeit aufgrund der erheblich höheren Verarbeitungstemperaturen. Die herkömmlichen Stahlwerkzeuge weisen durch Benetzung, Klebeneigung und Schmelzreaktionen einen hohen Verschleiß auf, woraus sehr geringe Werkzeugstandzeiten resultieren. Zielsetzung dieser Arbeit war die Entwicklung von prozessgerechten Werkzeugen zum Thixoschmieden von Stahl. Um geeignete Werkzeugtechnologien zu entwickeln, musste die gesamte Prozesskette des Verfahrens „Thixoschmieden von Stahl“ analysiert und optimiert werden. Grundsatzuntersuchungen, Formgebungsversuche und FEM- Simulationen zeigen, dass die Keramik Si3N4 sehr gut als Werkzeugwerkstoff geeignet ist. Durch Verwendung von vorgewärmten keramischen Werkzeugen, Optimierung der Bolzenerwärmung mit Schutzgas und vor allem durch die Entwicklung der Methode der gezielten Bolzenabkühlung können thixogeschmiedete Bauteile auf dem Qualitätsniveau von geschmiedeten Bauteilen hergestellt werden. Das Verfahren Thixoschmieden von Stahl bietet sehr große Einsparpotentiale, da der Zerspanungsaufwand stark reduziert werden kann und die Prozesskette durch zum Beispiel eine Umformung mit integrierter Fügung [KAL-02] oder Oberflächenvergütung [BEY-05] reduziert werden kann.
|l ger
520 _ _ |a In the process Thixoforging (forging in the semi-solid state) the advantages of the processes forging and casting can be combined. For example, complex geometries, which are normally produced in 4 or 5 steps, can be realised in one or two steps. In contrast to the forming of aluminium alloys in the semi-solid state, the forming of steel in the semi-solid state is much more difficult, because of the higher forming temperature. Common tools out of steel show a very important wear due to wetting, bonding and melting processes, which result in a very short tool life. The aim of this work was the development of appropriate tools for the thixoforming of steel. To develop appropriate tool technologies the entire process chain had to be analysed and optimised. Principle studies, forming tests and FEM-simulations show that the ceramic Si3N4 is very suitable as a material tool. The use of preheated tools of ceramic, the optimisation of the heating of billets with inert gas and particularly the development of the method of the aimed cooling before forming made possible the thixoforming of components with the same quality as forged ones. The process of thixoforming of steel offers very large potentials of cost savings, since the amount of machining work can be reduced and the process chain can be shortened for example by forming with an integrated joining process [KAL-02] or surface hardening.
|l eng
591 _ _ |a Germany
650 _ 7 |2 SWD
|a Thixogießen
650 _ 7 |2 SWD
|a Thixoforming
650 _ 7 |2 SWD
|a Thixoschmieden
650 _ 7 |2 SWD
|a Thixotropie
650 _ 7 |2 SWD
|a Schmieden
650 _ 7 |2 SWD
|a Umformwerkzeug
650 _ 7 |2 SWD
|a Umformen
650 _ 7 |2 SWD
|a Massivumformen
650 _ 7 |2 SWD
|a Matrize
653 _ 7 |a Ingenieurwissenschaften
653 _ 7 |2 ger
|a Bolzenabkühlung
653 _ 7 |2 ger
|a Si3N4-Keramik
653 _ 7 |2 ger
|a Armierungsauslegung
653 _ 7 |2 ger
|a Dauerbetrieb
653 _ 7 |2 eng
|a billet cooling
653 _ 7 |2 eng
|a Si3N4-ceramic
653 _ 7 |2 eng
|a semi-solid forming
700 1 _ |0 P:(DE-82)000834
|a Kopp, Reiner
|b 1
|e Thesis advisor
856 4 _ |u https://publications.rwth-aachen.de/record/61578/files/61578_kardex.pdf
|y Internal catalog entry
856 4 _ |u https://publications.rwth-aachen.de/record/61578/files/Beyer_Christophe.pdf
|y OpenAccess
856 4 _ |u https://publications.rwth-aachen.de/record/61578/files/61578_kardex.gif?subformat=icon
|x icon
|y Internal catalog entry
856 4 _ |u https://publications.rwth-aachen.de/record/61578/files/61578_kardex.jpg?subformat=icon-180
|x icon-180
|y Internal catalog entry
856 4 _ |u https://publications.rwth-aachen.de/record/61578/files/61578_kardex.jpg?subformat=icon-700
|x icon-700
|y Internal catalog entry
909 C O |o oai:publications.rwth-aachen.de:61578
|p openaire
|p open_access
|p urn
|p driver
|p VDB
|p dnbdelivery
915 _ _ |0 StatID:(DE-HGF)0510
|2 StatID
|a OpenAccess
920 1 _ |0 I:(DE-82)523410_20140620
|k 523410
|l Lehrstuhl und Institut für Bildsame Formgebung
|x 0
920 1 _ |0 I:(DE-82)520000_20140620
|k 520000
|l Fachgruppe für Materialwissenschaft und Werkstofftechnik
|x 1
970 _ _ |a HT014800991
980 1 _ |a FullTexts
980 _ _ |a phd
980 _ _ |a VDB
980 _ _ |a UNRESTRICTED
980 _ _ |a ConvertedRecord
980 _ _ |a FullTexts
980 _ _ |a I:(DE-82)523410_20140620
980 _ _ |a I:(DE-82)520000_20140620

LibraryCollectionCLSMajorCLSMinorLanguageAuthor
Marc 21