697662 20230408005231.0 Germany I:(DE-82)150000_20140620 I:(DE-82)151210_20140620 UNRESTRICTED VDB phd FullTexts 2 EndNote Thesis PUB:(DE-HGF)11 PUB:(DE-HGF) Dissertation / PhD Thesis phd phd BibTeX PHDTHESIS DRIVER doctoralThesis DataCite Output Types/Dissertation ORCID DISSERTATION P:(DE-82)IDM00073 Okuda, Jun 1 Thesis advisor rwth P:(DE-82)IDM00144 Richtering, Walter 2 Thesis advisor rwth RWTH-2017-07207 http://publications.rwth-aachen.de/record/697662/files/697662.pdf OpenAccess http://publications.rwth-aachen.de/record/697662/files/697662_source.zip Restricted http://publications.rwth-aachen.de/record/697662/files/AV_697662.docx Restricted http://publications.rwth-aachen.de/record/697662/files/AV_697662.doc Restricted http://publications.rwth-aachen.de/record/697662/files/AV_697662.odt Restricted http://publications.rwth-aachen.de/record/697662/files/697662.gif?subformat=icon icon OpenAccess http://publications.rwth-aachen.de/record/697662/files/697662.jpg?subformat=icon-180 icon-180 OpenAccess http://publications.rwth-aachen.de/record/697662/files/697662.jpg?subformat=icon-700 icon-700 OpenAccess Mikrogele aus isotaktischem Poly(styrol) lassen sich in einer Öl-Wasser-Emulsion durch Vernetzung des Polymers synthetisieren. Während dieses Prozesses entstehen Mikrogele mit Partikeldurchmessern von 40 nm bis 500 nm. Sie haben eine weiche Oberfläche, Poren einer Größe von ca. 7 nm und abhängig vom Vernetzungsgrad Domänen, die in getrockneter Form kristalline Eigenschaften aufweisen. Zur Bindung von Metall-Komplexen an die Mikrogele wurden zunächst funktionelle Gruppen an die linearen Polymere angebracht. Dabei wurden zwei Synthesewege genauer untersucht: Die Funktionalisierung einer Endgruppe im isotaktischen Poly(styrol) und die Copolymerisation von Styrol mit Styrol-Derivaten. Bei der Copolymerisation von Styrol und 4-(Fluorenylmethyl)styrol bleibt die hohe Isotaktizität auch im Copolymer erhalten und an den Fluorenyl-Substituenten konnte nach Deprotonierung ein Metall-Komplex der Gruppe 4 angebracht werden. ger Micorgels based on isotactic poly(styrene) can be synthesized through crosslinking of the polymer in an oil-in-water emulsion. During this process microgels with different particle diameters from 40 nm to 500 nm are formed. Their surface is soft and they possess pores with a size of approximately 7 nm. Depending on the degree of crosslinking these microgels have domains which show crystalline properties in dry form. For binding metal complexes to the microgels, functional groups were attached to linear polymers, at first. Two synthetic pathways were investigated in greater detail: the functionalization of endgroups in isotactic poly(styrene) and the copolymerization of styrene with some of it’s derivatives. High isotacticity is retained during copolymerization of styrene and 4-(fluorenylmethyl)styrene. To the fluorenyl substituent a group 4 metal complex was attached after deprotonation of the fluorenyl substituent. eng Diss. StatID:(DE-HGF)0510 StatID OpenAccess 2017 Dissertation, RWTH Aachen University, 2017 Dissertation RWTH Aachen University 2017 Fak01 2017-04-28 I:(DE-588b)36225-6 P:(DE-82)481942 RWTH Aachen 0 RWTH I:(DE-588b)36225-6 P:(DE-82)IDM00073 RWTH Aachen 1 RWTH I:(DE-588b)36225-6 P:(DE-82)IDM00144 RWTH Aachen 2 RWTH Veröffentlicht auf dem Publikationsserver der RWTH Aachen University 1 Online-Ressource (ii, 116 Seiten) : Illustrationen, Diagramme 540 Dataset connected to Lobid/HBZ Synthese und Funktionalisierung von Mikrogelen auf Basis von isotaktischem Poly(styrol) vorgelegt von Marie Tschage online HBZ HT019415020 Laufende Nummer 36354 datacite_doi 10.18154/RWTH-2017-07207 Aachen 2017 P:(DE-82)481942 Tschage, Marie 0 rwth German oai:publications.rwth-aachen.de:697662 openaire open_access VDB driver dnbdelivery I:(DE-82)151210_20140620 151210 Lehrstuhl für Metallorganische Chemie und Institut für Anorganische Chemie 0 I:(DE-82)150000_20140620 150000 Fachgruppe Chemie 1